SUS304L Stainless Steel is Japan under the standard of austenitic Stainless Steel and austenitic Stainless Steel SUS304L nonmagnetic and has high toughness and plasticity, but strength is low, cannot by phase transformation strengthening, can only through the cold working reinforcement, such as S, Ca, Se, Te elements, such as good free cutting.
SUS304L Stainless Steel Equivalent material
|
EN 10028-7/ EN10088-2 |
ASTM A240 |
JISG4304/4312 |
GB4237/4238 |
|
1.4306 |
304L |
SUS 304L |
00Cr19Ni10 |
SUS304L Stainless Steel Chemical Composition
|
Chemical Element |
% Present |
|
Carbon (C) |
0.0 - 0.03 |
|
Chromium (Cr) |
17.50 - 19.50 |
|
Manganese (Mn) |
0.0 - 2.00 |
|
Silicon (Si) |
0.0 - 1.00 |
|
Phosphorous (P) |
0.0 - 0.05 |
|
Sulphur (S) |
0.0 - 0.03 |
|
Nickel (Ni) |
8.00 - 10.50 |
|
Nitrogen (N) |
0.0 - 0.11 |
|
Iron (Fe) |
Balance |
SUS304L Stainless Steel Physical Property
|
Physical Property |
Value |
|
Density |
8.0 g/cm³ |
|
Melting Point |
1450 °C |
|
Thermal Expansion |
17.2 x10^-6 /K |
|
Modulus of Elasticity |
193 GPa |
|
Thermal Conductivity |
16.2 W/m.K |
|
Electrical Resistivity |
0.72 x10^-6 Ω .m |
SUS304L austenitic stainless steel has good production process performance, and by the conventional means of producing special steel, all kinds of plates, pipes, belts, forgings and castings of common specifications can be produced smoothly. Since alloying element (especially chromium) content is high and carbon content is low, arc furnace plus AOD or VOD is mainly used to produce SUS304L stainless steel in large quantities. For small batch products of high grade, it can be smelted in vacuum or non-vacuum non-induction furnace, and electroslag remelting is added when necessary.