We can offer S235JR steel,EN10025-2 S235JR carbon structure steel plate stock in China.
EN10025-2 S235JR Specification :
EN10025-2 S235JR is a kind of non-alloy structure steel.EN10025-2 S235JR steel is in the standard EN10025-2EN10025-2 series steel grades include : S235JR(J0,J2) S275JR(J0,J2) S355JR(J0,J2) S355JR(J0,J2,K2) S450J0.EN10025-2 series steel grade is a kind of common carbon structural steel, can be used in constructional , tank, building , bridge, machine .
Standard:EN10025-2
Steel Grade : S235JR(J0,J2) S275JR(J0,J2) S355JR(J0,J2) S355JR(J0,J2,K2) S450J0
Dimension range :1.5 mm -680mm x 1000mm-4000mm x 1000mm-18000mm
MOQ: 1 PC
Delivery time : Promptly ( Stock) or 10-40 days (Production)
Stock : Available
MTC: Available
Payment Term : T/T or L/C At sight .
EN10025-2 S235JR (1.0038) steel equivalent material:
EN10025-2 S235JR (1.0038) steel equivalent material |
|
DIN17100
St 37-2 |
GB/T700 Q235B |
NFA 35-501
E 24-2 |
BS 4360
40A |
UNI 7070
Fe 360 B |
ASTM A283 C ASTM A570 Gr. 33 |
EN10025-2 S235JR steel chemical composition (%) :
Grade |
Material No. |
Killed or not |
C ≤ |
Si ≤ |
Mn≤ |
P≤ |
S≤ |
N≤ |
Cu≤ |
|
Thickness (mm) |
|
≤16 |
＞16~ 40 |
＞40 |
|
S235JR |
1.0038 |
Semi-killed or killed |
0.17 |
0.17 |
0.20 |
- |
1.40 |
0.035 |
0.035 |
0.012 |
0.55 |
EN10025-2 S235JR (1.0038) Chemical composition of the Product analysis :
Nominal thickness =< 30(mm)
CEV max = 0.35 Nominal thickness from 30 to 40 (mm)
CEV max = 0.35 Nominal thickness from40 to 150 (mm)
CEV max = 0.38 Nominal thickness from150 to 250 (mm)
CEV max = 0.40
For long products the P and S content can be 0.005% higher
For long products the max. S content can be increased for improved machinability by 0,015 % by agreement if the steel is treated to modify the sulphide morphology and the chemical composition shows min. 0,0020 % Ca.
The max. value for nitrogen does not apply if the chemical composition shows a minimum total Al content of 0,015 %or alternatively min. 0,013 % acid soluble Al or if sufficient other N binding elements are present. In this case the N binding elements shall be mentioned in the inspection document.
Cu content above 0,45 % may cause hot shortness during hot forming.
If other elements are added, they shall be mentioned on the inspection document.
For nominal thickness > 150 mm: C = 0,22 % max.
For grades suitable for cold roll forming (see 7.4.2.2.3): C = 0,24 % max.
For nominal thickness > 30 mm: C = 0,24 % max.
Applicable for long products only.
EN10025-2 S235JR steel Mechanical properties :
Nominal thickness (mm) |
to 16 |
16 - 40 |
40 - 63 |
63 - 80 |
80 - 100 |
100 -150 |
150 - 200 |
200-250 |
|
Yield strength Min(MPa) |
235 |
225 |
215 |
215 |
215 |
195 |
185 |
175 |
|
Nominal thickness (mm) |
to 3 |
3-100 |
100-150 |
150-250 |
|
Tensile strength (MPa) |
360-510 |
360-510 |
360-510 |
350-500 |
|
Nominal thickness (mm) |
To 1 |
1-1.5 |
1.5-2 |
2-2.5 |
2.5-3 |
|
Minimum elongation
Lo = 5,65 √ So (%) |
17 |
18 |
19 |
20 |
21 |
We are professional EN10025-2 steel stockist and supplier. We can supply different product type and good quality EN10025-2 steel.We can offer you S235JR,S235J0,S235J2,S275JR,S275J0,S275J2 structure steel .If you have any need of EN10025-2 steel please do not hesitate to contact us .